Push-Out Bond Strength of Glass Fiber Endodontic Posts with Different Diameters

(1) Background: The retention of intraradicular posts is an important factor for the prognosis of endodontically treated teeth. The purpose of this study was to evaluate the push-out bond strength (PBS) of the posts relating to their diameter and region of the root. (2) Methods: A total of 40 premol...

Teljes leírás

Elmentve itt :
Bibliográfiai részletek
Szerzők: Rajnics Zsolt
Pammer Dávid
Kőnigné Péter Anikó
Turzó Kinga Mónika
Marada Gyula
Radnai Márta
Dokumentumtípus: Cikk
Megjelent: 2024
Sorozat:MATERIALS 17 No. 7
Tárgyszavak:
doi:10.3390/ma17071492

mtmt:34771068
Online Access:http://publicatio.bibl.u-szeged.hu/34132
Leíró adatok
Tartalmi kivonat:(1) Background: The retention of intraradicular posts is an important factor for the prognosis of endodontically treated teeth. The purpose of this study was to evaluate the push-out bond strength (PBS) of the posts relating to their diameter and region of the root. (2) Methods: A total of 40 premolar teeth (decoronated and root canal-filled) were divided into four groups (n = 10). After post-space preparation, different sizes (1.0, 1.2, 1.5, and 2.0 mm) of glass fiber posts were luted with resin cement into the root canals. After placement, 2 mm thick slices were cut from the roots according to their apical, middle, and coronal regions (n = 116). Push-out tests were carried out in a universal testing machine on each slice. A statistical evaluation of the data was applied. (3) Results: When comparing the diameter, the 2.0 mm posts had the highest PBS (111.99 ± 10.40 N), while the 1.0 mm posts had the lowest PBS (99.98 ± 8.05 N). Divided by the surface of the bonded area, the average PBS value was the highest for the 1.0 mm posts (18.20 ± 1.67 MPa) and the lowest for the 2.0 mm posts (12.08 ± 1.05 MPa). (4) Conclusions: Within the limitations of the study, when comparing the regions of the roots, no significant differences were found among the PBS values of the three regions (p = 0.219). When comparing the diameters, significant differences were shown between the PBS values of the four groups (p = 0.023 and p = 0.003, respectively).
Terjedelem/Fizikai jellemzők:10
ISSN:1996-1944