Fatigue behavior of endodontically treated premolars restored with different fiber-reinforced designs

Objectives: The aim was to investigate the fatigue survival and marginal-gap inside the root-canal of endodontically treated (ET) premolars reinforced by various fiber-reinforced post-core composites (FRCs). Moreover, composite-curing at different depths in the canal was evaluated. Methods: 170 inta...

Full description

Saved in:
Bibliographic Details
Main Authors: Fráter Márk Tibor
Sáry Tekla
Jókai Blanka
Braunitzer Gábor
Säilynoja Eija
Vallittu Pekka K.
Lassila Lippo
Garoushi Sufyan
Format: Article
Published: 2021
Series:DENTAL MATERIALS 37 No. 3
doi:10.1016/j.dental.2020.11.026

mtmt:31803239
Online Access:http://publicatio.bibl.u-szeged.hu/20951
Description
Summary:Objectives: The aim was to investigate the fatigue survival and marginal-gap inside the root-canal of endodontically treated (ET) premolars reinforced by various fiber-reinforced post-core composites (FRCs). Moreover, composite-curing at different depths in the canal was evaluated. Methods: 170 intact upper-premolars were collected and randomly divided into ten groups (n = 15). One group served as control (intact-teeth). After endodontic procedure standard MO cavities were prepared and restored with different post-core fiber-reinforced materials and designs. Three-group (A1-A3) were restored with either packable and flowable short fiber-reinforced composite (SFRC) core or conventional composite-core. Two-group (B1-B2) were restored with SFRCs as short post (3 mm) and core. Four-group (C1-C4) were restored with SFRCs as post (6 mm) and core with or without unidirectional FRC posts (individually-made or conventional). After completing the restorations, teeth from Group C1-C4 (n = 5/group) were sectioned and stained. Specimens were viewed under a stereo-microscope and the percentage of microgaps within the root-canal was calculated. Fatigue-survival was measured using a cyclic-loading machine in the rest of the specimens. Results: Application of flowable SFRC as luting-core material with individually-made FRC post (Group C3) did not differ from intact-teeth regarding fatigue-survival (p > 0.05). The rest of the groups produced significantly lower survival (p < 0.05) compared to intact-teeth. Post/core restorations made from packable SFRC (Group C1) had a lower microgap (19.1%) at the examined interphase in the root-canal than other groups. Significance: The restoration of ET premolars with the use of individually-made FRC post and SFRC as luting-core material showed promising achievement regarding fatigue-resistance and survival. © 2020 The Academy of Dental Materials
Physical Description:391-402
ISSN:0109-5641